Kaowool Ceramic Paper (Kaowool1260)
Note : Pre-order item
Kaowool Ceramic Paper
Ceramic paper is manufactured from high purity refractory fibres and designed for high temperature insulation.
Advanced production techniques ensure uniform fibre distribution and close control of thickness and density.
Ceramic paper is produced from Alumina-Silicate fibres with the minimum addition of carefully selected bonds, which burn out cleanly in service.
Type : Refractory Ceramic Fibre Paper
Classification Temperature : 1260°C
The maximum continuous use temperature depends on the application.
Advantages :
- Good resistance to tearing
- High flexibility
- Low shot content
- Precise thickness
- Resistant to thermal shock
- Very low thermal conductivity
Applications :
- Insulating thermal break
- Insulating gaskets
- Expansion joints
- Parting media
- Die cut gaskets for domestic appliances
- Thermal barriers for vehicles (silencers, catalytic exhausts and heat shields)
- Fire protection
Main Properties :
Classification temperature | °C | 1260 |
|
|
|
Typical Physical Properties |
|
|
Colour |
| white |
Density | Kg/m3 | 190 |
Melting point (minimum) | °C | 1760 |
Tensile strength | kN/m2 | 750 |
Thickness measurement pressure | kPa | 10 |
|
|
|
High Temperature Performance |
|
|
Binder content/loss on ignition | % | 8 |
Shrinkage (24 hours at 1260°C) | % | 3.5 |
Thermal conductivity (BS 1902 Part 6) at mean temperature of: |
|
|
200°C | W/m.K | 0.06 |
300°C | W/m.K | 0.07 |
400°C | W/m.K | 0.09 |
500°C | W/m.K | 0.11 |
600°C | W/m.K | 0.13 |
800°C | W/m.K | 0.20 |
Indicative heat loss table :
Hot Face | Insulation Thickness | ||||
0.5 mm | 1.0 mm | 2.0 mm | 4.0 mm | 8.0 mm | |
538°C | 400 | 335 | 268 | 202 | 145 |
649°C | 471 | 395 | 316 | 239 | 172 |
760°C | - | 456 | 364 | 276 | 200 |
871°C | - | 516 | 413 | 315 | 229 |
982°C | - | - | 462 | 353 | 258 |
1093°C | - | - | 510 | 393 | 290 |
1204°C | - | - | - | 433 | 321 |
1260°C | - | - | - | 453 | 337 |
Chemical composition :
Al₂0₃ % 47
Si0₂ % 52
Other oxides % 1
Combustibility
Alumino-Silicate refractory fibres are non-combustible when tested in accordance with BS 476, Part 4.
The values given herein are typical values obtained in accordance with accepted test methods and are subject to normal manufacturing variations. They are supplied as a technical service and are subject to change without notice.
Packaging size :
| Thickness ( mm ) |
| 1.0 |
| 2.0 |
| 3.0 |
| 4.0 |
| 5.0 |
| 6.0 |
| 8.0 |
| 10.0 |
Terms & Conditions :
- The above picture is for illustration only
- All the above descriptions are subject to change without notice
- Delivery : approx. 7 to 10 working days ( Peninsular Malaysia )
approx. 2 to 3 working weeks ( Sabah, Labuan & Sarawak, subject to courier delivery schedule ) - Warranty : No
For enquiries, kindly contact us @
Tel : +6012 728 1063
Email : enquiry@giitechnology.com